Austenitic · Stainless Steel
Low-Carbon Austenitic Stainless Steel 304L
Chemical composition and mechanical properties per ASTM A240; available sizes are standard ranges.
① Chemical Composition (ASTM A240, %)
| Element | Range |
|---|---|
| C | ≤0.03 |
| Si | ≤0.75 |
| Mn | ≤2.00 |
| P | ≤0.045 |
| S | ≤0.030 |
| Cr | 18.0–20.0 |
| Ni | 8.0–12.0 |
② Mechanical Properties (ASTM A240)
| Property | Requirement |
|---|---|
| Tensile Strength Rm | ≥ 485 MPa |
| Yield Strength Rp0.2 | ≥ 170 MPa |
| Elongation A | ≥ 40% |
| Hardness | ≤ 201 HBW |
③ Available Sizes (Standard Range)
- Thickness: 0.3–60 mm
- Width: ≤ 2000 mm
- Form: Coils / Sheets / Plates / Discs / Slit Strips on request
- Surface: 2B · BA · No.1 · No.4 · HL · 8K on request
④ Applicable Standards
ASTM A240 · EN 10088-2 · JIS G4304/4305 · GB/T 3280
⑤ Typical Applications
Thick-walled welded components, large tanks, chemical equipment, piping, and welded fittings not subjected to post-weld heat treatment
⑥ Substitution & Selection Tips
Slightly lower strength than 304 but better intergranular corrosion resistance after welding. If solution annealing is applied after welding, 304 is sufficient.
Chemical and mechanical data are quoted from the general ASTM A240 standard. Available sizes are standard ranges; the contract and technical agreement shall prevail.